利用低温NMR技术测定木材及其热处理材纤维饱和点

doi:10.11938/cjmr20170113

波谱学杂志 ›› 2017, Vol. 34 ›› Issue (1): 108-114.doi: 10.11938/cjmr20170113

• 低场磁共振技术与应用专栏 • 上一篇下一篇

利用低温NMR技术测定木材及其热处理材纤维饱和点

周凡丁¹, 高鑫², 蔡家斌¹, 庄寿增¹, 周洪杰¹

1. 南京林业大学材料科学与工程学院, 江苏南京 210037;
2. 中国林科院木工研究所, 北京 100091

收稿日期:2015-12-30 修回日期:2017-01-09 出版日期:2017-03-05 发布日期:2017-03-05
通讯作者: 蔡家斌,Tel:13505179534,E-mail:nldfloor@163.com E-mail:nldfloor@163.com
基金资助:
江苏高校优势学科建设工程资助项目（PAPD）

Determination of Treated and Control Wood on Fiber Saturation Point by Low-Field NMR Technology

ZHOU Fan-ding¹, GAO Xin², CAI Jia-bin¹, ZHUANG Shou-zeng¹, ZHOU Hong-jie¹

1. College of Materials Science and Technology, Nanjing Forestry University, Nanjing 210037, China;
2. Research Institute of Wood Industry, Chinese Academy of Forestry, Beijing 100091, China

Received:2015-12-30 Revised:2017-01-09 Online:2017-03-05 Published:2017-03-05

摘要/Abstract

摘要： 实验基于核磁共振技术（Nuclear Magnetic Resonance，NMR）检测的无损性，利用低场NMR技术测定热处理前后花旗松的纤维饱和点（Fiber Saturation Point，FSP）.在-3℃和25℃条件下，对CPMG（Carr-Purcell-Meiboom-Gill）脉冲测得的信号进行横向弛豫时间（T²）分析，对比试样冷冻前后信号反演峰面积，确定试样吸着水饱和含量，得到不同热处理条件下花旗松的纤维饱和点依次为38.76%（对照材）、32.82%（180℃热处理）、29.40%（200℃热处理）、24.90%（220℃热处理）.实验结果表明，热处理温度越高，纤维饱和点越低.该结果测试结果与木材学理论相符，表明NMR技术可应用于快速确定木材纤维饱和点.

关键词: 纤维饱和点(FSP), 横向弛豫时间(T²), 热处理, 核磁共振(NMR)

Abstract: Due to its non-destructive characteristic, nuclear magnetic resonance (NMR) spectroscopy was used to study the fiber saturation point (FSP) of Pseudotsuga menziesii before and after heat treatment. The bound water amount in saturated wood cell wall was determined by analysis of T² relaxation time distributions measured using GPMG (Carr-Purcell-Meiboom-Gill) sequence at -3℃ and 25℃. Results showed that the FSP of Pseudotsuga menziesii treated with various temperatures are 32.82% (180℃), 29.40% (200℃), 24.90% (220℃) and 38.76% (untreated), which indicate that FSP of Pseudotsuga menziesii decreases with increased heat treatment temperature. This study reflects that NMR could provide detailed information about wood water distribution rapidly and efficiently.

Key words: T² relaxation time, nuclear magnetic resonance (NMR), heat treatment, fiber saturation point (FSP)

中图分类号:

O482.53

周凡丁, 高鑫, 蔡家斌, 庄寿增, 周洪杰. 利用低温NMR技术测定木材及其热处理材纤维饱和点[J]. 波谱学杂志, 2017, 34(1): 108-114.

ZHOU Fan-ding, GAO Xin, CAI Jia-bin, ZHUANG Shou-zeng, ZHOU Hong-jie. Determination of Treated and Control Wood on Fiber Saturation Point by Low-Field NMR Technology[J]. Chinese Journal of Magnetic Resonance, 2017, 34(1): 108-114.

参考文献

[1] HILL C A S. Wood modification:Chemical, thermal and other processes[M]. Chichester:Wiley, 2006
[2] XIE Y, QILIANG F, QINGWEN W, et al. Effects of chemical modification on the mechanical properties of wood[M]. Eur J Wood Prod, 2003, 71(4):401-416
[3] LIAO G Z, XIAO L Z. Research on porous of exponential inversion Factors Influencing by NMR relaxation measurements[J]. Geophysics, 2007, 50(3):932-983. 廖广志, 肖立志. 孔隙介质核磁共振弛豫测量多指数反演影响因素研究[J]. 地球物理学报, 2007, 50(3):932-983
[4] GAO X, ZHUANG S Z. Bound water content in saturated wood cell wall determined by nuclear magnetic resonance spectroscopy[J]. Chinese J Magn Reson, 2015, 32(4):671-676. 高鑫, 庄寿增. 利用核磁共振测木材吸着水饱和含量[J]. 波谱学杂志, 2015, 32(4):671-676.
[5] BABIAK M, KUDELA. A contribution to the definition of the fiber saturation point[J]. Wood Sci, Technol, 29(3):217-226.
[6] TELKKI V V, YLINIEMI M, JOKISAARI J. Moisture in softwoods:Fiber saturation point,hydroxyl site contentand the amount ofmicropores as determined from NMR relaxation time distributions[J]. Holzforschung, 2013, 67(3):291-300.
[7] MA D Y, WANG X M, ZHANG M H. Mechanism of water sorption during adsorptionprocess of wood studied by NMR[J]. Chinese J of Magn Reson, 2011, 28(1):135-141. 马大燕, 王喜明, 张明辉. 核磁共振研究木材吸着过程水分吸附机理[J]. 波谱学杂志, 2011, 28(1):135-141.
[8] AKSNES D W, KIMTYS L. ¹H and ²H NMR studies of benzene confined in porous solids:Melting point depression and poresizedistribution[J]. Solid State Nucl Mag, 2004, 25(1-3):146-152.
[9] LI C, ZHANG M H, YU J F. Determining wood moisture content by free inductiondecay of nuclear magnetic resonance[J]. Journal of Beijing Forestry University, 2012, 34(4):142-145. 李超, 张明辉, 于建芳. 利用核磁共振自由感应衰减曲线测定木材含水率[J]. 北京林业大学学报, 2012, 34(4):142-145.
[10] 肖立志. 核磁共振成像测井与岩石核磁共振及其应用[M]. 北京:科学出版社, 1998.
[11] KEKKONEN P M, YLISASSI A, TELKKI V V. Absorption of water in thermally modified pine wood as studied by nuclear magnetic resonance[J]. J Phys Chem C, 2004, 118(4):2146-2153.
[12] SIMPSON L A, BARTON A F M. Determination of the fiber saturation point in whole wood using differential scanning calorimetry[J]. Wood Sci, Technol, 1991, 25:301-308.
[13] ZAUER M, KRETZSCHMAR J, GROBMANN L, et al. Analysis of the pore-size distribution and fiber saturationpoint of native and thermally modified wood using differential scanning calorimetry[J]. Wood Sci Technol, 2014, 48(1):177-193.
[14] 赵喜平. 磁共振成像系统的原理及其应用[M]. 北京:科学出版社, 2000.
[15] DING T, GU L B, LIU X. Influence of steam pressure on chemical changes of heat-treated Mongolian pine wood[J]. Bio Resources, 2011, 6(2):1880-1889.
[16] Rowell R M. Handbook of wood chemistry and wood composites[M]. Boca Raton:CRC Press, 2005.
[17] GINDL W, ZARGAR-YAGHUBI F, WIMMER R. Impregnation of softwood cell walls with melamine-formaldehyde resin[J]. Bioresour Technol, 2003, 87(3):325-330.
[18] ZHANG S C, QI H C. Effect of high temperature steam treatment on the crystalline properties of wood[J]. Journal of Nanjing Forestry University, 2010, 34(5):164-166. 张士成, 齐华春. 高温过热蒸汽处理对木材结晶性能的影响[J]. 南京林业大学学报:自然科学版, 2010, 34(5):164-166.
[19] BHUIYAN M T R, HIRAI N, SOBUE N. Changes of crystallinity in wood cellulose by heat treatment under driedandmoist conditions[J]. J Wood Sci, 2000, 46(6):431-436.
[20] AKGÜL M, GÜMÜSKAYA E, KORKUT S. Crystalline structure of heattreated Scots pine (Pinus sylvestrisL) a-nd Uluda ? fir[Abies nordmanniana (Stev.)subsp.bornmuelleriana(Mattf.)] wood[J]. Wood Sci Technol, 2007, 41(3):281-289.
[21] TJEERDSMA B F, BOONSTRA M, PIZZI A, et al. Characterisation of thermally modified wood:Molecular reasons for wood performance improvement[J]. Holz als Roh-und Werkstoff, 1998, 56(3):149-153.
[22] WEILAND J J, GUYONNET R. Study of chemical modifications and fungi degradation of thermally modified wood using DRIFT spectroscopy[J]. Holz als Roh-und Werkstoff, 2003, 61(3):216-220.
[23] WIKBERG H, MAUNU S L. Characterisation of thermally modied hard-and softwoods by ¹³C CPMAS NMR[J]. Carbohydrate Polymers, 2004, 58(4):461-466.
[24] BORREGA M K, RENLAMPI P P. Hygroscopicity of heat-treated Norway spruce (Picea abies) wood[J]. Holz als Roh-und Werkstoff, 2010, 68(2):233-235.
[25] JACKSON C L, MCKENNA G B. The melting behavior of organic materials confined in porous solid[J]. Chem Phys, 93:9002-9011.
[26] WANG Z P, WANG T. The principle and application of NMR freezing hole method[J]. Journal of material, 2013, 27(1):129-133. 王中平, 王弢. 简述核磁共振冷冻测孔法的原理及应用[J]. 材料导报, 2013, 27(1):129-133.
[27] OSTLUND A, KOHNKE T, NORDSTIERNA L, et al. NMR cryopormetry to study the fiber wall structure and the effect of drying[J]. Cellulose, 2010, 17:321-328.
[28] KEKKONEN P M, YLISASSI A, TELKKI V V. Absorption of water in thermally modified pine wood as studied by NMR[J]. J Phys Chem C, 2013, 118:2146-2153.

利用低温NMR技术测定木材及其热处理材纤维饱和点

Determination of Treated and Control Wood on Fiber Saturation Point by Low-Field NMR Technology

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	胡坤, 孙汉董, 普诺·白玛丹增. 量子化学计算核磁共振参数在天然产物结构鉴定中的应用[J]. 波谱学杂志, 2019, 36(3): 359-376.
[2]	尹田鹏, 王雅溶, 王敏, 石文智, 张正茜, 何莎莎. 三个C₁₉-二萜生物碱的NMR数据全归属[J]. 波谱学杂志, 2019, 36(3): 331-340.
[3]	杨云汉, 杜瑶, 应飞祥, 杨俊丽, 夏大真, 夏福婷, 杨丽娟. 柚皮素/β-环糊精超分子体系的包合行为[J]. 波谱学杂志, 2019, 36(3): 319-330.
[4]	王亚兰, 王晓静, 王志伟. 阿齐沙坦的波谱学数据及结构确证[J]. 波谱学杂志, 2019, 36(3): 350-358.
[5]	曹园, 吴永平, 陈东军. 卷柏属Selaginellin类化合物互变异构的波谱学研究[J]. 波谱学杂志, 2019, 36(2): 155-163.
[6]	陈晓瑛, 俞刚金, 毛诗珍, 刘买利, 杜有如. 利用¹H NMR探究混合离子型/非离子型表面活性剂临界胶束浓度降低的实质[J]. 波谱学杂志, 2019, 36(2): 219-224.
[7]	寇新慧, 刘乙祥, 刘兴弘, 李从刚, 刘买利, 姜凌. 探测应答调控蛋白PhoB_N^F20D自由态中存在的Pre-Active构象[J]. 波谱学杂志, 2019, 36(2): 164-171.
[8]	迟秀娟, 乔晓亚, 刘颖, 刘惠丽, 陈雷, 王际辉, 艾选军. 拟南芥AtGrp7 RRM结构域的纯化及其结构与结合的初步分析(英文)[J]. 波谱学杂志, 2019, 36(1): 1-14.
[9]	尹田鹏, 汪泽, 陈阳, 邵娅婷, 邓亮, 黎唯. 10-吲哚细胞松弛素chaetoglobosin F的NMR解析[J]. 波谱学杂志, 2019, 36(1): 74-82.
[10]	尹田鹏, 罗智慧, 蔡乐, 丁中涛. 天然C₁₉-二萜生物碱的研究进展及其核磁共振波谱特征[J]. 波谱学杂志, 2019, 36(1): 113-126.
[11]	冉梦琳, 覃凌云, 唐淳, 董旭. 磷酸化调控泛素单体与Rad23A/Ubiquilin-1中泛素结合域互作的检测[J]. 波谱学杂志, 2019, 36(1): 15-22.
[12]	魏会强, 于江, 毕常芬, 宁洪鑫, 李祎亮, 刘强. N-异丁酰基-3'-O-(1-氟-1,1,3,3-四异丙基-1,3-二硅氧烷-3-基)-2'-苄氧羰基鸟苷的NMR研究[J]. 波谱学杂志, 2019, 36(1): 93-102.
[13]	李英俊, 杨凯栋, 靳焜, 刘季红, 王思远, 张楠. 基于咔唑-靛红双-硫代碳酰腙衍生物的NMR研究[J]. 波谱学杂志, 2019, 36(1): 83-92.
[14]	王伟宇, 胡涵, 徐君, 邓风. Pd-Cu双金属催化剂上加氢反应的仲氢诱导超极化研究[J]. 波谱学杂志, 2018, 35(3): 269-279.
[15]	朱云峰, 何为, 何传红, 王怡, 齐天昊, 陈柏冰, 徐征. 基于数字调制技术的核磁共振射频脉冲发生器[J]. 波谱学杂志, 2018, 35(3): 318-327.