钠、硼酸盐玻璃的11B变温核磁共振研究

波谱学杂志 ›› 1990, Vol. 7 ›› Issue (1): 115-118.

钠、硼酸盐玻璃的¹¹B变温核磁共振研究

徐曙, 潘麟章, 邬学文

华东师范大学物理系

收稿日期:1989-03-16 修回日期:1989-06-17 出版日期:1990-03-05 发布日期:2018-01-23
基金资助:
国家自然科学基金

TEMPERATURE-DEPENDENT ¹¹B NMR STUDIES OF SODIUM BORATE GLASSES

Xu Shu, Pan Linzhang, Wu Xuewen

Department of Physics, East China Normal University, Shanghai

Received:1989-03-16 Revised:1989-06-17 Online:1990-03-05 Published:2018-01-23

摘要/Abstract

摘要： 本文应用变温¹¹B核磁共振技术研究了RNa₂O·B₂O₃玻璃体系在室温和300℃时硼原子的配位情况。结果表明,当R>0.5时,四配位硼原子数随温度的上升而减少。因此,玻璃态结构也可能随温度变化而改变。

关键词: 变温核磁共振, 玻璃态, 玻璃转变温度

Abstract: Temperature-dependent ¹¹B NMR technics have been employed to determine the boron coordination in sodium borate glasses at room temperature and 300℃.The results show that, as R>0.5, the fraction of borons in 4-coordinated will decrease as temperature increases. These resuhs mean that it is possible for glass structure changes as temperature is below the transitional temperature.

Key words: Temperature-dependent NMR, Vitreous, Transitional temperature

徐曙, 潘麟章, 邬学文. 钠、硼酸盐玻璃的¹¹B变温核磁共振研究[J]. 波谱学杂志, 1990, 7(1): 115-118.

Xu Shu, Pan Linzhang, Wu Xuewen. TEMPERATURE-DEPENDENT ¹¹B NMR STUDIES OF SODIUM BORATE GLASSES[J]. Chinese Journal of Magnetic Resonance, 1990, 7(1): 115-118.

[1]	朱传钧, 金晓锋, 姜标, 崔育新. 奥拉西坦的核磁共振波谱特征与构象研究[J]. 波谱学杂志, 2010, 27(4): 609-616.
[2]	章宪权, 吴肖令, 邬学文. 玻璃和晶体粉末样品的核磁共振谱的计算机拟合[J]. 波谱学杂志, 1988, 5(2): 129-140.
[3]	戴胜, 陈克. S为1/2体系粉末或冷冻玻璃态电子自旋共振谱的模拟[J]. 波谱学杂志, 1987, 4(1): 21-27.

钠、硼酸盐玻璃的¹¹B变温核磁共振研究

TEMPERATURE-DEPENDENT ¹¹B NMR STUDIES OF SODIUM BORATE GLASSES

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 3

编辑推荐

Metrics

本文评价